Hyaluronic acid doped-poly(3,4-ethylenedioxythiophene)/chitosan/gelatin (PEDOT-HA/Cs/Gel) porous conductive scaffold for nerve regeneration

Research paper by Shuping Wang, Shui Guan, Zhibo Zhu, Wenfang Li, Tianqing Liu, Xuehu Ma

Indexed on: 18 Oct '16Published on: 17 Oct '16Published in: Materials Science and Engineering: C



Abstract

Conducting polymer, as a “smart” biomaterial, has been increasingly used to construct tissue engineered scaffold for nerve tissue regeneration. In this study, a novel porous conductive scaffold was prepared by incorporating conductive hyaluronic acid (HA) doped-poly(3,4-ethylenedioxythiophene) (PEDOT-HA) nanoparticles into a chitosan/gelatin (Cs/Gel) matrix. The physicochemical characteristics of Cs/Gel scaffold with 0–10 wt% PEDOT-HA were analyzed and the results indicated that the incorporation of PEDOT-HA into scaffold increased the electrical and mechanical properties while decreasing the porosity and water absorption. Moreover, in vitro biodegradation of scaffold displayed a declining trend with the PEDOT-HA content increased. About the biocompatibility of conductive scaffold, neuron-like rat phaeochromocytoma (PC12) cells were cultured in scaffold to evaluate cell adhesion and growth. 8% PEDOT-HA/Cs/Gel scaffold had a higher cell adhesive efficiency and cell viability than the other conductive scaffolds. Furthermore, cells in the scaffold with 8 wt% PEDOT-HA expressed higher synapse growth gene of GAP43 and SYP compared with Cs/Gel control group. These results suggest that 8%PEDOT-HA/Cs/Gel scaffold is an attractive cell culture conductive substrate which could support cell adhesion, survival, proliferation, and synapse growth for the application in nerve tissue regeneration.

Graphical abstract 10.1016/j.msec.2016.10.029.jpg
Figure 10.1016/j.msec.2016.10.029.0.jpg
Figure 10.1016/j.msec.2016.10.029.1.jpg
Figure 10.1016/j.msec.2016.10.029.2.jpg
Figure 10.1016/j.msec.2016.10.029.3.jpg
Figure 10.1016/j.msec.2016.10.029.4.jpg
Figure 10.1016/j.msec.2016.10.029.5.jpg
Figure 10.1016/j.msec.2016.10.029.6.jpg